7005 Aluminum block cut to size

Time :2020/02/10 Click :
The introduce of 7005 Aluminum block cut to size
Name:7005 Aluminum block cut to size
Temper: 7005
Material Name : Deformed aluminum and aluminum alloy
Standard Control Alcoa Association (AA) 7005
7005 Aluminum block cut to size belongs to the Al-Zn-Mg-Cu super hard aluminum, good welding performance, heat treatment can be strengthened, the strength of less than 6061, but a lot of light, is a typical lightweight aluminum. 7005 Aluminum block cut to size, often used in making welded structure have both high strength and high fracture toughness, such as transport vehicles, truss rod, container; large heat exchanger, and after welding can not be solid melt processing components; also can be used in the manufacture of sports equipment such as tennis racket and baseball bat.

7005 Aluminum block
 
7005 Aluminum block cut to size standard control
American Aluminum Association (AA) 7005, UNS A97005;
China GB 7005;
Japan JIS (7N11)
 
The chemical composition of 7005 Aluminum block cut to size
Al (minimum): margin
Si: ≤0.35
Fe: ≤ 0.40
Cu: ≤ 0.10
Mn: 0.20~0.7
Mg: 1.0~1.8
Cr: 0.06~0.20
Zn: 4.0~5.0
Zr: 0.08~0.20
Ti: 0.01~0.06
Other elements not specified: each: ≤ 0.05; total: ≤ 0.15
 
Performance advantage of 7005 Aluminum block cut to size
1, 7005 Aluminum block cut to size has good mechanical and anodic reaction, high strength and heat treatment;
2, 7005 Aluminum block cut to size has good mechanical properties, easy processing, good wear resistance;
3, The use of good, after the elimination of stress, deformation and warpage after processing. All 7005 aluminum by ultrasonic detection, can ensure no blisters, impurities;
4, Especially for the manufacture of aircraft structures and other requirements of high strength, corrosion resistance of high stress structure;